Flash butt welding-flashing, Mechanical Engineering

Assignment Help:

Flash Butt Welding-Flashing

The phenomenon of flashing is of extreme importance in achieving satisfactory welds. Flashing can begin only after a molten bridge has been formed somewhere along the interface. If the parts fit accurately, difficulty in initiating the process may be experienced and it may be necessary to level the butting surfaces to give local contact. This procedure is much different from that for resistance pressure welding where a good fit is desirable to exclude the atmosphere and prevent surface contamination. In the flash welding, surface contamination is removed in the spatter during flashing and molten metal is expelled in the final upset or forging operation.

Once a molten bridge has been formed it is set in motion over the interface by the electrodynamic forces resulting from the distortion of the current path through the work pieces. While it traverses over interface at a speed of 10 cm / s, more heat is generated in the bridge by the joule effect and is lost to the colder metal at each end. Assuming the bridge does not freeze, it will be broken in one of two ways. It may either explode because of the combined influence of overheating and the pinch effect or it may race to the edge of the work piece where it becomes extended in the form of an arc between the work faces until it ruptures. In either event, much of the metal contained in the bridge is propelled out of the joint as spatter.

Because, there is inevitably considerable inductance in the secondary circuit, collapsing of the electrical field at rupture results in a voltage surge which is capable to initiate an arc, although the open circuit voltage cannot sustain it and it is rapidly extinguished.

The Considerable heat is generated in these brief arcing periods which accounts for the efficiency of the process compared with resistance butt welding.


Related Discussions:- Flash butt welding-flashing

Cast iron, CAST IRON: Cast iron is an important alloy of Fe and C are ...

CAST IRON: Cast iron is an important alloy of Fe and C are mostly employed within industry for its convenience to casting in intricate and superior mechanical properties. Stee

Thermal, diference between thermal and thermodynamic equallibrim

diference between thermal and thermodynamic equallibrim

Determine the centroidal moment of inertia, Determine the centroidal moment...

Determine the centroidal moment of inertia: Determine the centroidal moment of inertia of a thin flat disc shown in Figure which is having a mass m kg. By using the parallel a

What is the velocity of the crosshead - crank, What is the velocity of the ...

What is the velocity of the crosshead - crank: In the slider crank mechanism shown in Figure, the crank is rotating clockwise at 120 revolution/minute. What is the velocity of

Determine velocity at a cross section of the pipe, Consider a fully develop...

Consider a fully developed laminar flow of a fluid through a 200 m long and 4 cm diameter horizontal and circular pipe. The density and the viscosity of the fluid are 1400 kg/m 3

Enthalpy - thermodynamics, Enthalpy: Sol: The enthalpy is total ener...

Enthalpy: Sol: The enthalpy is total energy of gaseous system. It takes into consideration, internal energy and pressure, volume effect. Thus, it can be defined as follows:

Describe the mechanics of orthogonal cutting, Describe the Mechanics of ort...

Describe the Mechanics of orthogonal cutting. What is chip thickness ratio and formulae for it ? Explain Shear angle relationship based on Merchant's minimum cutting energy prin

Cement, wet process of portland cement

wet process of portland cement

Mechanics materials , 1) Factor of Safety is calculated by using which of t...

1) Factor of Safety is calculated by using which of the following set of values? [Select the one best answer from the choices given below.] Answer a. Yield Stress and Allowable St

Schedule selection -schedule evaluation-heuristics, Schedule Evaluation ...

Schedule Evaluation The schedules are evaluated as per to the criterion weighted loss of slack. Now let t 0 si be the slack (time buffer) of job I as per to the initial sched

Write Your Message!

Captcha
Free Assignment Quote

Assured A++ Grade

Get guaranteed satisfaction & time on delivery in every assignment order you paid with us! We ensure premium quality solution document along with free turntin report!

All rights reserved! Copyrights ©2019-2020 ExpertsMind IT Educational Pvt Ltd