Q. Alloy materials control?
All low alloy and high alloy equipment components including fittings, flanges and sections of pipe and all welds shall be individually tested by Vendor to verify alloy content after assembly of Equipment or Component is completed.
The alloy content for both welds and fittings shall be within the range specified for the base metal, per applicable ASME or ASTM specification.
Frequency of testing shall be as follows:
• One test per fitting, flange, plate, head and each attachment to pressure parts.
• One test per circumferential seam and one test per longitudinal seam.
Q. What is Extrusion defects? • Surface cracking - When the surface of an extrusion splits. This is often caused by the extrusion temperature, friction, or speed being too high
Q. Materials used in insulation? All materials must be non-corrosive, compatible with other materials and used in accordance with the Manufacturer's recommendations. All mat
TERMINOLOG Y: 1 . Top dead and Bottom dead Centre: These are 2 extreme positions between which the piston reciprocates inside the cylinder. TDC and BDC have relevance
Goods Market and the IS Curve The IS curve shows the combinations of interest rates and levels of output such that planned spending equals income. In order to derive the IS cur
First law of thermodynamics applied to flow process
Q. Selection of Electrodes and Filler Metals? Only low hydrogen electrodes shall be used for SMAW of all carbon and low alloy steels, except for root pass welding of single wel
Q. What do you know about Direct welds? It is a welding method in which one or more electrodes oppose each other, contacting both sides of the work and with the current passing
Cam This is a mechanical member that imparts motion to another member called follower. Illustration: A cam is rotating at regular speed of 1200 rpm in the clockwise d
Mas s Flow Rate (m ): In absence of any mass getting stored system we can write; Mass flow rate at inlet = Mass flow rate at outlet That is, m f1 = m f2 as m f = d
Effect of the parameters in spot welding The passage of more current than what is required causes the following defects. I. Weld expulsion ii. Cavitations iii. Weld cracking
Get guaranteed satisfaction & time on delivery in every assignment order you paid with us! We ensure premium quality solution document along with free turntin report!
whatsapp: +91-977-207-8620
Phone: +91-977-207-8620
Email: [email protected]
All rights reserved! Copyrights ©2019-2020 ExpertsMind IT Educational Pvt Ltd