Yield strength for alloy that has average grain diameter

Assignment Help Mechanical Engineering

Reference no: EM13709616

The yield strength for an alloy that has an average grain diameter of 4.4 x 10^-2 mm is 115 MPa. At a grain diameter of 7.1 x 10^-3 mm, the yield strength increases to 258 MPa. At what grain diameter, in mm, will the yield strength be 237 MPa?

Reference no: EM13709616

Questions Cloud

Determine the maximum speed reached by the mass : An electric hoist consumes 5 kW of power at a constant rate to lift a 500-kg mass. Assuming that the hoist is 80% efficient, determine the maximum speed reached by the mass.

Changes in kinetic and potential energies are negligible : Air is compressed steadily in a compressor from 100kPa and 300 K to 1 Mpa and 500 K. The compressor is not well insulated and a heat loss of 40 KJ/kg occurs during the process. Assuming the changes in kinetic and potential energies are negligible, de..

Monthly payment if the mortgage is to be paid off : You are buying a home for $360000. If you make a down payment of $60000 ad take out a mortgage on the rest at 8.5% compounded monthly, what will be your monthly payment if the mortgage is to be paid off in 15 years?

Room is heated by a base-board resistance heater : Room is heated by a base-board resistance heater, which is designed to heat the air in this room from 8oC to 27 oC within 20 min. Approximating the room as a thermo-insulated cuboid 15m ? 10m ? 5m and assuming the specific heats to be constant at a r..

Yield strength for alloy that has average grain diameter : The yield strength for an alloy that has an average grain diameter of 4.4 x 10-2 mm is 115 MPa. At a grain diameter of 7.1 x 10-3 mm, the yield strength increases to 258 MPa. At what grain diameter, in mm, will the yield strength be 237 MPa?

Brass is higher than recrystallization temperature of copper : According to the Hall-Petch equation, Ostwald ripening follows the empirical rule. The recrystallization temperature of brass is higher than the recrystallization temperature of copper. The recrystallization temperature of bronze is lower than the re..

Length of dislocation line per unit volume in material equal : The length of dislocation line per unit volume in a material equals the number of dislocations per unit area. Metals are hardened by cold working because many of the dislocations have passed right through the grains and are no longer available to fac..

A piston-cylinder system initially contains an ideal gas : A piston-cylinder system initially contains an ideal gas at {State 1} After an isothermal expansion process, the pressure of the gas in the cylinder drops to P 2bar 2? Please draw a schematic of the process 1-2 on a

Calculate the post-deformation radius of the second specimen : Two fully annealed cylindrical specimens of an alloy are to be hardened by reducing their (always circular) cross-sections in an extrusion process. For one specimen, the initial and post-deformation radii are 15mm and 12 mm, respectively.

User Account

All Pages