What was the yield stress of your brass after reduction

Assignment Help Mechanical Engineering

Reference no: EM13708979

A brass rod 1.5 cm in diameter is deformed in tension reducing its diameter to 1.128 cm. The data for brass in Fig. 7.19 will be helpful in solving this problem.

a) If the deformation process was performed in one step, what was the yield stress of your brass after reduction?

b) Again assuming one step, what was the force applied to your specimen (in N) at the very end of the reduction process? Assume you applied just enough force to make the material yield.

c) If your deformation equipment is able to apply a force of 35,000 N to your specimen, could you accomplish your deformation process in one step? Please explain your answer.

d) If you cannot accomplish your deformation process in one step, what must you do to reduce the diameter of the brass rod to 1.128 cm? No, you can't afford to purchase a bigger machine?

Reference no: EM13708979

Questions Cloud

Successfully navigated the marketing process : Details: Over the past three weeks you have successfully navigated the marketing process. You have an understanding of your customer needs and the marketing environment through research. You have developed a marketing strategy and begun develop..

Determine the mass flow rate of the steam : Steam enters an adiabatic turbine at 5 MPa, 650°C, and 80 m/s and leaves at 50 kPa, 150°C, and 140 m/s. If the power output of the turbine is 8 MW, determine (a) the mass flow rate of the steam flowing through the turbine and (b) the isentropic effic..

Scrum vs plan-based software development strategies : Develop a visual rendering of each approach using Microsoft Visio or its open source alternative, Dia. Note: The graphically depicted solution is not included in the required page length.

Determine the isentropic efficiency of the compressor : Air is compressed by an adiabatic compressor from 95 kPa and 27°C to 600 kPa and 277°C. Assuming variable specific heats and neglecting the changes in kinetic and potential energies, determine (a) the isentropic efficiency of the compressor and (b) t..

What was the yield stress of your brass after reduction : A brass rod 1.5 cm in diameter is deformed in tension reducing its diameter to 1.128 cm. The data for brass in Fig. 7.19 will be helpful in solving this problem. If the deformation process was performed in one step, what was the yield stress of your ..

Determine the entropy generated and shows sgen varies : The brake of a vehicle can be modeled as a solid of mass m , with specific heat c and uniform temperature T , initially equal to the ambient temperature T0. During the braking process the brake receives work input W, temperature rises to T and heat t..

Determine what the heat flux would be in terms : If you have a plane wall separating hot and cold fluids at temperature T(infinity)1 & T(infinity)2. Using x=0 & x=L as boundary conditions, determine what the heat flux would be in terms of T(infinity)1, T(infinity)2, h1, h2, k, L.

Manufacturing does not require a final shaping operation : manufacturing does not require a final shaping operation. Cooling the outer layer of ceramic quickly may leave it in residual. Ceramics based on SiO2 are known as

Determine the total flow exergy rates at the valve inlet : Water vapor enters a valve with a mass flow rate of 1 kg/s at a temperature of 260 degrees C and a pressure of 3.5 MPa, and undergoes a throttling process to 2.75 MPa (T0=25, P0=100kPa).

User Account

All Pages