What is the final wafer thickness after thermal oxidation

Assignment Help Mechanical Engineering

Reference no: EM131255610

The surface of a silicon wafer is thermally oxidized, resulting in a SiO2 film that is 100 nm thick. If the starting thickness of the wafer was exactly 0.400 mm, what is the final wafer thickness after thermal oxidation?

Reference no: EM131255610

Questions Cloud

Confidential negotiations with another company : Your company is engaged in confidential negotiations with another company. In what wayscould rivals use sniffing to get this commercially sensitive data? For each way say what youcould do to minimise the risk.

Describe a memorable occasion in your own life experience : Socrates, Plato, Aristotle, Lucretius. Compose a well-motivated question that any one of these ancient philosophers would, if given the chance, propose to any one of the others. Make sure to explain the motivation of the inquirer using evidence fr..

Estimate the value of all of the ic chips : The processable area of each wafer is defined by a diameter = 270 mm. Estimate the value of all of the IC chips that could be produced, assuming an overall yield of 80% good product.

Examples of some common thermocouples : Explain the principle of a thermocouple. Give two examples of some common thermocouples.

What is the final wafer thickness after thermal oxidation : The surface of a silicon wafer is thermally oxidized, resulting in a SiO2 film that is 100 nm thick. If the starting thickness of the wafer was exactly 0.400 mm, what is the final wafer thickness after thermal oxidation?

Develop a strategic analysis for this organization : For your strategic analysis assignment, you should choose an organization that you are familiar with. You will develop a strategic analysis for this organization in order to determine whether or not adopting a new sustainability initiative is poss..

Describe the organizational environment or corporate culture : Does the Code of Professional provide helpful guidance as to how the dilemma should be addressed? If so, cite the provision that gave guidance. Describe the organizational environment or corporate culture in which the dilemma exists. Cite Kohlb..

Hard magnetic material : Draw the hysteresis loop for a soft magnetic material and compare it with the hysteresis loop of hard magnetic material. Give two examples of each.

What should be the size of the mask opening : If plasma etching is used instead of wet etching, and the degree of anisotropy for plasma etching is infinity, what should be the size of the mask opening?

User Account

All Pages