Calculate the post-deformation radius of the second specimen

Assignment Help Mechanical Engineering

Reference no: EM13709612

Two fully annealed cylindrical specimens of an alloy are to be hardened by reducing their (always circular) cross-sections in an extrusion process. For one specimen, the initial and post-deformation radii are 15mm and 12 mm, respectively. The second specimen has an initial radius of 11 mm, and is required to end up with the same hardness as the first specimen when both have been deformed.

Calculate the post-deformation radius of the second specimen.

Reference no: EM13709612

Questions Cloud

Yield strength for alloy that has average grain diameter : The yield strength for an alloy that has an average grain diameter of 4.4 x 10-2 mm is 115 MPa. At a grain diameter of 7.1 x 10-3 mm, the yield strength increases to 258 MPa. At what grain diameter, in mm, will the yield strength be 237 MPa?

Brass is higher than recrystallization temperature of copper : According to the Hall-Petch equation, Ostwald ripening follows the empirical rule. The recrystallization temperature of brass is higher than the recrystallization temperature of copper. The recrystallization temperature of bronze is lower than the re..

Length of dislocation line per unit volume in material equal : The length of dislocation line per unit volume in a material equals the number of dislocations per unit area. Metals are hardened by cold working because many of the dislocations have passed right through the grains and are no longer available to fac..

A piston-cylinder system initially contains an ideal gas : A piston-cylinder system initially contains an ideal gas at {State 1} After an isothermal expansion process, the pressure of the gas in the cylinder drops to P 2bar 2? Please draw a schematic of the process 1-2 on a

Calculate the post-deformation radius of the second specimen : Two fully annealed cylindrical specimens of an alloy are to be hardened by reducing their (always circular) cross-sections in an extrusion process. For one specimen, the initial and post-deformation radii are 15mm and 12 mm, respectively.

Assuming the casting approximates semi-infinite medium : A large plastic casting with thermal diffusivity 6.0 x10^7 m2 /s is removed from its mold at a uniform temperature of 150 degrees C. The casting is then exposed to a high-velocity air stream such that the surface experiences a sudden change in temper..

Stresses required to prevent vertical edges from displacing : Resolve the problem below with the vertical edges constrained from displacing in x direction, but free to displace vertically. Determine the vertical displacement of the top edge and the stresses required to prevent the vertical edges from displacing..

Surface concentration during diffusion : For diffusion of Cu into Al at 1000 K for 10 hours, calculate the distance into the material at which the concentration of Cu will be 5% if the initial concentration of Cu in the Aluminium was 0.5% and the surface concentration during diffusion was 5..

Determine the change in pressure between these two locations : At a certain position in a piping system, a fluid with a specific gravity of 1.50 passes through an 8-cm diameter pipe with a velocity of 1.2 m/s. At some point downstream the elevation of the pipe has increased by 15 m and the pipe size has been red..